回顧了國內(nèi)外近幾十年來關(guān)于Zircaloys合金中第二相粒子本征特征(晶體結(jié)構(gòu)、成分、形狀、亞結(jié)構(gòu)等)的相關(guān)研究工作。
鋯合金第二相研究述評(Ⅰ)：Zircaloys合金Review of second phase particles on zirconium alloys (Ⅰ): Zircaloys
回顧了國內(nèi)外近幾十年來關(guān)于Zircaloys合金中第二相粒子本征特征(晶體結(jié)構(gòu)、成分、形狀、亞結(jié)構(gòu)等)的相關(guān)研究工作。 Zircaloys合金中的Zr-Fe-Ni粒子只有一種，即C16(BCT，Al2Cu)型Zr2(Fe, Ni) Zintl相。而Zr-Fe-Cr粒子主要有兩種：一種是C14(HCP, MgZn2)型Zr(Fe, Cr)2?Laves相，另一種是C15(FCC, MgCu2)型Zr(Fe, Cr)2?Laves相，這些Laves相內(nèi)部均可見層錯結(jié)構(gòu)。歸納總結(jié)出形成溫度決定論、n(Fe)/n(Cr)決定論、價電子/原子比決定論3種理論，用于解釋Zr(Fe, Cr)2粒子形成穩(wěn)定結(jié)構(gòu)的原因。常規(guī)加工工藝下，在Zircaloys合金成分范圍內(nèi)，Sn完全固溶于α-Zr基體，不會參與形成析出相，F(xiàn)e、Cr、Ni一般也不會單獨與Zr形成Zr-Fe、Zr-Cr、Zr-Ni粒子。
In the recent decades the investigations about intrinsic characteristics (crystallographic structure, microchemistries, shape, substructure, etc.) of the second phase particles (SPPs) that might present in Zirclaoys were thoroughly reviewed. Some research experiences and approaches which would be of great help to the SPPs investigations for new-developed high-performance zirconium alloys are obtained. It can be summarized that in Zircaloys there is only one kind of Zr-Fe-Ni SPPs, i.e. C16 (BCT, Al2Cu) Zr2(Fe, Ni) Zintl phase. While for the Zr-Fe-Cr Laves SPPs in zircaloys, there are two variants. One is C14 (HCP, MgZn2) Zr(Fe, Cr)2?and the other is Laves phase with C15 (FCC, MgCu2) structure. Stacking faults were frequently observed by researchers in those Zr(Fe, Cr)2SPPs. Based on a large amount of studies, it is summarized that the formation temperature, n(Fe)/n(Cr) ratios or valence electron/atom ratios of SPPs are determinant factors in respect to the stable structures of Zr(Fe, Cr)2. In addition, the possibility of presence of Sn-bearing particles was discussed as well as Zr-Fe, Zr-Cr and Zr-Ni particles in Zircaloys under conventionally processing conditions.
以上資料由上海艾荔艾金屬材料有限公司提供，歡迎新老客戶來電洽購。
本文來自上海艾荔艾金屬材料有限公司http://www.85978597.cn，轉(zhuǎn)載請注明出處。