基于腐蝕環(huán)境和基材相互作用機(jī)理，結(jié)合管材、腐蝕產(chǎn)物、水質(zhì)等因素，分析了某20G無縫鋼管穿孔泄漏失效原因。
20G無縫鋼管穿孔泄漏失效分析Failure Analysis on Perforation Leakage of 20G Seamless Steel Tube基于腐蝕環(huán)境和基材相互作用機(jī)理，結(jié)合管材、腐蝕產(chǎn)物、水質(zhì)等因素，分析了某20G無縫鋼管穿孔泄漏失效原因。結(jié)果表明：鋼管穿孔泄漏主要是由于管內(nèi)介質(zhì)環(huán)境引起20G無縫鋼管發(fā)生局部腐蝕，水質(zhì)較差偏硬， Cl-和F-等腐蝕性離子的存在促進(jìn)了點(diǎn)蝕環(huán)境的形成，導(dǎo)致無縫鋼管穿孔泄漏。建議改善水質(zhì)處理及監(jiān)測，并采用耐點(diǎn)蝕的Cr-Mo低合金鋼管替代現(xiàn)有20G鋼管。
Based on interaction mechanism of the corrosion environment and the material itself and combined factors such as material, corrosion products, water quality and so on, the perforation leakage reasons of 20G seamless steel tube were analyzed. The results show that the perforation leakage of the 20G seamless steel tube was the result of local corrosion caused by the tube inner medium environment. The poor and hard water quality and existence of corrosive ions Cl- and F- promoted the formation of pitting environment and resulted in the perforation leakage. It was proposed to improve water quality treatment and monitoring and use of pitting corrosion resistance of Cr-Mo low alloy steel instead of the existing material.
作為值得信賴的合作伙伴和高品質(zhì)金屬合金的半成品供應(yīng)商，艾荔艾擁有完善的服務(wù)體系和專業(yè)的團(tuán)隊(duì)。在同客戶交易的過程中，我們力求根據(jù)不同的應(yīng)用需求將我們的產(chǎn)品做到精益求精。針對當(dāng)前和未來的市場需求，艾荔艾致力于為客戶提供最佳的金屬材料解決方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
獲取更多我們供應(yīng)的合金和服務(wù)信息，請致電086-021-67660801或發(fā)電子郵件kefu@ailiaigroup.com聯(lián)系我們，您也可以通過微博，微信，領(lǐng)英，XING，臉書和推特與我們互動。
For more information on the alloys and services that we supply,?call us?at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on?Weibo,?Weixin,?LinkedIn,?XING, Facebook?and?Twitter.